PA6-C100 (CAS No.None)
- 物化性质
- 密度1.13 g/cm³，饱和吸水率11%（23℃），平衡吸水率3.0%（23℃，50%RH）。拉伸模量2600 MPa，断裂拉伸应力70.0 MPa，断裂拉伸应变>50%，弯曲强度100 MPa，简支梁缺口冲击强度2.5 kJ/m²（23℃），无缺口冲击无断裂。热变形温度145℃（0.45 MPa，未退火），55.0℃（1.8 MPa，未退火），维卡软化温度>200℃，熔融温度220℃，UL94阻燃等级V-2（1.60 mm和3.20 mm）。表面电阻率1.0E+14 ohms，体积电阻率1.0E+15 ohm·cm，漏电起痕指数600 V。
- 密度
- 1.13 g/cm³（ISO 1183）
English description（英文原文，共 1410 字符）
Product Name:PA6-C100
English Name:PA6-C100
CAS No.:25038-54-4
Aliases:Nylon 6, Polycaprolactam, PA6
Molecular Formula:(C6H11NO)n
Physical Properties:Density 1.13 g/cm³, saturated water absorption 11% (23℃), equilibrium water absorption 3.0% (23℃, 50%RH). Tensile modulus 2600 MPa, tensile stress at break 70.0 MPa, tensile strain at break >50%, flexural strength 100 MPa, Charpy notched impact strength 2.5 kJ/m² (23℃), unnotched impact no break. Heat deflection temperature 145℃ (0.45 MPa, unannealed), 55.0℃ (1.8 MPa, unannealed), Vicat softening temperature >200℃, melting temperature 220℃, UL94 flame rating V-2 (1.60 mm and 3.20 mm). Surface resistivity 1.0E+14 ohms, volume resistivity 1.0E+15 ohm·cm, comparative tracking index 600 V.
Uses:Suitable for thin-wall parts and equipment/machine components. This material has excellent flowability and is suitable for injection molding, enabling the production of thin-wall products with complex structures or high precision requirements.
Technical Specifications:
Density: 1.13 g/cm³ (ISO 1183)
Tensile modulus: 2600 MPa; tensile stress at break: 70.0 MPa; tensile strain at break: >50% (ISO 527-2)
Flexural strength: 100 MPa (ISO 178)
Heat deflection temperature: 145℃ (0.45 MPa, unannealed, ISO 75-2/B); Vicat softening temperature: >200℃ (ISO 306/B)
Flame rating: UL94 V-2 (1.60 mm and 3.20 mm); surface resistivity: 1.0E+14 ohms (IEC 60093)
English Name:PA6-C100
CAS No.:25038-54-4
Aliases:Nylon 6, Polycaprolactam, PA6
Molecular Formula:(C6H11NO)n
Physical Properties:Density 1.13 g/cm³, saturated water absorption 11% (23℃), equilibrium water absorption 3.0% (23℃, 50%RH). Tensile modulus 2600 MPa, tensile stress at break 70.0 MPa, tensile strain at break >50%, flexural strength 100 MPa, Charpy notched impact strength 2.5 kJ/m² (23℃), unnotched impact no break. Heat deflection temperature 145℃ (0.45 MPa, unannealed), 55.0℃ (1.8 MPa, unannealed), Vicat softening temperature >200℃, melting temperature 220℃, UL94 flame rating V-2 (1.60 mm and 3.20 mm). Surface resistivity 1.0E+14 ohms, volume resistivity 1.0E+15 ohm·cm, comparative tracking index 600 V.
Uses:Suitable for thin-wall parts and equipment/machine components. This material has excellent flowability and is suitable for injection molding, enabling the production of thin-wall products with complex structures or high precision requirements.
Technical Specifications:
Density: 1.13 g/cm³ (ISO 1183)
Tensile modulus: 2600 MPa; tensile stress at break: 70.0 MPa; tensile strain at break: >50% (ISO 527-2)
Flexural strength: 100 MPa (ISO 178)
Heat deflection temperature: 145℃ (0.45 MPa, unannealed, ISO 75-2/B); Vicat softening temperature: >200℃ (ISO 306/B)
Flame rating: UL94 V-2 (1.60 mm and 3.20 mm); surface resistivity: 1.0E+14 ohms (IEC 60093)
共 1 家生产厂家、批发商，
1 条供应报价
供应报价
常见问题
- PA6-C100的 CAS 号是多少？
- PA6-C100的 CAS 号是 None。
- PA6-C100的分子式和分子量是什么？
- PA6-C100的分子式为 (C6H11NO)n。
- PA6-C100的英文名称是什么？
- PA6-C100的英文名称为 PA6-C100。
- PA6-C100还有哪些别名？
- PA6-C100又称 尼龙6、聚己内酰胺、PA6。
- PA6-C100有哪些供应商和生产厂家？
- 掌上化工当前收录 1 条PA6-C100供应报价，来自 1 家供应商，可按地区、纯度、级别筛选对比。
- PA6-C100的供应商主要分布在哪些地区？
- PA6-C100的供应商主要分布在 上海市（1 条） 等地。
- PA6-C100有哪些级别可选？
- 平台上PA6-C100的供应级别包括 工业级。
- PA6-C100的报价单位是什么？
- PA6-C100的报价单位主要有 千克。
- 哪里可以查到PA6-C100的价格？
- 掌上化工PA6-C100产品页汇总了各供应商的最新报价与规格，地址：/chemicals/pa6-c100/。部分供应商价格为电议，可通过页面上的询价功能直接获取。
以上信息由平台根据收录的产品数据自动生成，数据更新时间 。 价格与库存由供应商自行发布，实际交易请以询价结果为准。
没找到合适的供应商？
发布采购需求，让供应商主动联系你。我们会在 1 个工作日内跟进。
发布PA6-C100采购需求