PA66 Latamid 66 B G/20-V (CAS No.None)

Product Name:PA66 Latamid 66 B G/20-V

English Name:PA66 Latamid 66 B G/20-V

CAS No.:32131-17-2

Aliases:Polyamide 66, Nylon 66, Poly(hexamethylene adipamide)

Molecular Formula:(C12H22N2O2)n

Physical Properties:This product is a flame-retardant reinforced PA66 (polyamide 66) material. Density is 1.52 g/cm³; mold shrinkage is 0.25%-0.45% in the flow direction and 0.7%-1.0% in the perpendicular direction; water absorption (23°C/24h) is 0.28%. Mechanical properties: tensile modulus 8100 MPa at 23°C and 2400 MPa at 150°C; tensile strength at break 115 MPa at 23°C; yield strength 45 MPa at 150°C; Charpy notched impact strength 3.5 kJ/m² at 23°C. It exhibits good flame retardancy, high-temperature resistance, and high flowability.

Uses:It is suitable for electronic and electrical applications, such as flame-retardant housings and connectors. It can also be used in automotive components requiring high-temperature resistance, such as engine surrounding parts. Its high flowability makes it ideal for injection molding complex industrial parts.

Technical Specifications:

Density: 1.52 g/cm³

Mold shrinkage: 0.25%-0.45% in flow direction, 0.7%-1.0% in perpendicular direction

Water absorption (23°C/24h): 0.28%

Tensile modulus: 8100 MPa at 23°C, 2400 MPa at 150°C

Mechanical properties: tensile strength at break 115 MPa (23°C), yield strength 45 MPa (150°C), Charpy notched impact strength 3.5 kJ/m² (23°C)