PC-6710 (CAS No.None)
- 物化性质
- 外观为清晰/透明颗粒，阻燃（UL94 V-0），RoHS合规。密度1.20 g/cm³，熔体流动速率(300°C/1.2 kg)为10 g/10 min，成型收缩率(流动)为0.50-0.70%。拉伸屈服强度61.8 MPa，断裂伸长率100%，弯曲模量2160 MPa，弯曲强度88.3 MPa，悬壁梁缺口冲击强度(23°C)为830 J/m；载荷下热变形温度(1.8 MPa)为125°C，维卡软化温度148°C；透光率>87%，雾度<1.2%。
- 技术参数
- 干燥温度120°C，干燥时间4.0 h。 料筒温度建议280-310°C，模具温度70-100°C。 UL94阻燃等级V-0（3.00 mm）。 透光率>87%，雾度<1.2%（2000 μm）。 比重1.20 g/cm³，熔体流动速率10 g/10 min（300°C/1.2 kg）。
English description（英文原文，共 1155 字符）
Product Name:Polycarbonate
English Name:Polycarbonate
CAS No.:25037-45-0
Aliases:PC, WONDERLITE PC-6710, Polycarbonate resin
Molecular Formula:(C16H14O3)n
Physical Properties:Clear/transparent appearance, flame retardant (UL94 V-0), RoHS compliant. Density 1.20 g/cm³, melt flow rate (300°C/1.2 kg) 10 g/10 min, mold shrinkage (flow) 0.50-0.70%. Tensile yield strength 61.8 MPa, elongation at break 100%, flexural modulus 2160 MPa, flexural strength 88.3 MPa, Izod notched impact strength (23°C) 830 J/m; heat deflection temperature under load (1.8 MPa) 125°C, Vicat softening temperature 148°C; light transmittance >87%, haze <1.2%.
Uses:Suitable for injection molding of electronic and electrical components as well as automotive interior and exterior parts, especially thin-wall products requiring transparency, flame retardancy, and dimensional stability.
Technical Specifications:
Drying temperature 120°C, drying time 4.0 h.
Barrel temperature recommended 280-310°C, mold temperature 70-100°C.
UL94 flame rating V-0 (3.00 mm).
Light transmittance >87%, haze <1.2% (2000 μm).
Density 1.20 g/cm³, melt flow rate 10 g/10 min (300°C/1.2 kg).
English Name:Polycarbonate
CAS No.:25037-45-0
Aliases:PC, WONDERLITE PC-6710, Polycarbonate resin
Molecular Formula:(C16H14O3)n
Physical Properties:Clear/transparent appearance, flame retardant (UL94 V-0), RoHS compliant. Density 1.20 g/cm³, melt flow rate (300°C/1.2 kg) 10 g/10 min, mold shrinkage (flow) 0.50-0.70%. Tensile yield strength 61.8 MPa, elongation at break 100%, flexural modulus 2160 MPa, flexural strength 88.3 MPa, Izod notched impact strength (23°C) 830 J/m; heat deflection temperature under load (1.8 MPa) 125°C, Vicat softening temperature 148°C; light transmittance >87%, haze <1.2%.
Uses:Suitable for injection molding of electronic and electrical components as well as automotive interior and exterior parts, especially thin-wall products requiring transparency, flame retardancy, and dimensional stability.
Technical Specifications:
Drying temperature 120°C, drying time 4.0 h.
Barrel temperature recommended 280-310°C, mold temperature 70-100°C.
UL94 flame rating V-0 (3.00 mm).
Light transmittance >87%, haze <1.2% (2000 μm).
Density 1.20 g/cm³, melt flow rate 10 g/10 min (300°C/1.2 kg).
共 1 家生产厂家、批发商，
1 条供应报价
供应报价
常见问题
- PC-6710的 CAS 号是多少？
- PC-6710的 CAS 号是 None。
- PC-6710的分子式和分子量是什么？
- PC-6710的分子式为 (C16H14O3)n。
- PC-6710的英文名称是什么？
- PC-6710的英文名称为 Polycarbonate。
- PC-6710还有哪些别名？
- PC-6710又称 PC、WONDERLITE PC-6710、聚碳酸酯树脂。
- PC-6710有哪些供应商和生产厂家？
- 掌上化工当前收录 1 条PC-6710供应报价，来自 1 家供应商，可按地区、纯度、级别筛选对比。
- PC-6710的供应商主要分布在哪些地区？
- PC-6710的供应商主要分布在 上海市（1 条） 等地。
- PC-6710有哪些级别可选？
- 平台上PC-6710的供应级别包括 工业级。
- PC-6710的报价单位是什么？
- PC-6710的报价单位主要有 千克。
- 哪里可以查到PC-6710的价格？
- 掌上化工PC-6710产品页汇总了各供应商的最新报价与规格，地址：/chemicals/pc-6710/。部分供应商价格为电议，可通过页面上的询价功能直接获取。
以上信息由平台根据收录的产品数据自动生成，数据更新时间 。 价格与库存由供应商自行发布，实际交易请以询价结果为准。
没找到合适的供应商？
发布采购需求，让供应商主动联系你。我们会在 1 个工作日内跟进。
发布PC-6710采购需求