PC/ABS合金料FR3310 TV (CAS No.None)

Product Name:FR3310 TV Polycarbonate + Acrylonitrile Butadiene Styrene

English Name:FR3310 TV Polycarbonate + Acrylonitrile Butadiene Styrene

Aliases:FR3310 TV, PC/ABS FR3310 TV, Flame-retardant glass fiber reinforced PC/ABS alloy

Physical Properties:PC/ABS alloy, 15% glass fiber reinforced, flame-retardant grade, RoHS compliant, suitable for injection molding. Density 1.28 g/cm³ (23°C); melt volume-flow rate 23.0 cm³/10min (260°C/5.0 kg); mold shrinkage (240°C/3.00 mm) 0.20-0.40% perpendicular to flow and 0.30-0.50% in flow direction; water absorption 0.40% saturated (23°C), 0.10% equilibrium (23°C/50% RH). Tensile modulus 5300 MPa, tensile stress at break 95.0 MPa, tensile strain at break 3.0%; Izod notched impact strength 8.0 kJ/m², unnotched impact strength 30 kJ/m². Heat deflection temperature 98.0°C (0.45 MPa), 92.0°C (1.8 MPa); Vicat softening temperature 98.0-100°C; linear thermal expansion coefficient 4.0E-5 cm/cm/°C (flow), 7.0E-5 cm/cm/°C (transverse). Surface resistivity 1.0E+16 ohm, volume resistivity 1.0E+16 ohm·cm, dielectric strength 35 kV/mm; relative permittivity 3.20 (100 Hz), 3.10 (1 MHz); dissipation factor 5.0E-3 (100 Hz), 7.0E-3 (1 MHz). UL94 flammability: V-1 at 1.20 mm, V-0 at 1.50 mm.

Uses:Suitable for injection-molded parts with high flame-retardancy requirements, such as electrical and electronic equipment housings, connectors and charging pile enclosures. Also used in automotive interior parts, instrument panel frames and other products requiring good dimensional stability and heat resistance.

Technical Specifications:

15% glass fiber reinforced, flame-retardant grade, RoHS compliant

Density 1.28 g/cm³ (23°C, ISO 1183)

Melt volume-flow rate 23.0 cm³/10min (260°C/5.0 kg, ISO 1133)

Tensile modulus 5300 MPa, tensile stress at break 95.0 MPa (23°C, ISO 527-2)

UL94 flammability rating: V-0 at 1.50 mm, V-1 at 1.20 mm