POM 2010 (CAS No.None)
- 物化性质
- 比重1.42 g/cm³；熔流率（190°C/2.16kg）1.7 g/10min；收缩率1.8-2.2%；吸水率0.20%；洛氏硬度M94/R120；拉伸模量2900 MPa；拉伸屈服应力70-75 MPa；断裂伸长率55%；弯曲模量2700-2720 MPa；弯曲强度97 MPa；简支梁缺口冲击强度15 kJ/m²；悬壁梁缺口冲击强度130 J/m；热变形温度0.45MPa下163-172°C，1.8MPa下100-130°C；线膨胀系数1.0E-4 cm/cm/°C；比热1470 J/kg/°C；导热系数0.23 W/m/K；表面电阻率1E16-1E17 ohms；体积电阻率1E15-1E16 ohm·cm；介电强度18 kV/mm；介电常数3.8（1MHz）；耗散因数7E-3（1MHz）；耐电弧性250s；UL阻燃等级HB。
- 密度
- 1.42 g/cm³（ASTM D792/ISO 1183）
English description（英文原文，共 1428 字符）
Product Name:Polyoxymethylene (POM) 2010
English Name:Polyoxymethylene (POM) 2010
CAS No.:9002-81-7
Aliases:Acetal Resin, Polyacetal, POM
Molecular Formula:(CH2O)n
Physical Properties:Specific gravity 1.42 g/cm³; Melt flow rate 1.7 g/10min (190°C/2.16 kg); Molding shrinkage 1.8-2.2%; Water absorption 0.20%; Rockwell hardness M94/R120; Tensile modulus 2900 MPa; Tensile stress at yield 70-75 MPa; Elongation at break 55%; Flexural modulus 2700-2720 MPa; Flexural strength 97 MPa; Charpy notched impact strength 15 kJ/m²; Izod notched impact strength 130 J/m; Heat deflection temperature 163-172°C at 0.45 MPa, 100-130°C at 1.8 MPa; Coefficient of linear thermal expansion 1.0E-4 cm/cm/°C; Specific heat 1470 J/kg/°C; Thermal conductivity 0.23 W/m/K; Surface resistivity 1E16-1E17 ohms; Volume resistivity 1E15-1E16 ohm·cm; Dielectric strength 18 kV/mm; Dielectric constant 3.80 (1 MHz); Dissipation factor 7.0E-3 (1 MHz); Arc resistance 250 s; UL flammability rating HB.
Uses:Mainly used to manufacture gears, conveyor machine parts, engineering parts and fasteners, as well as housings, bearings and other components in automotive applications.
Technical Specifications:
Density: 1.42 g/cm³ (ASTM D792/ISO 1183)
Melt flow rate: 1.7 g/10min (190°C/2.16kg, ISO 1133)
Tensile strength (yield): 70.0 MPa (ISO 527-2)
Heat deflection temperature: 130°C at 1.8 MPa (ASTM D648)
Flammability rating: HB (UL 94, 0.8mm/1.5mm)
English Name:Polyoxymethylene (POM) 2010
CAS No.:9002-81-7
Aliases:Acetal Resin, Polyacetal, POM
Molecular Formula:(CH2O)n
Physical Properties:Specific gravity 1.42 g/cm³; Melt flow rate 1.7 g/10min (190°C/2.16 kg); Molding shrinkage 1.8-2.2%; Water absorption 0.20%; Rockwell hardness M94/R120; Tensile modulus 2900 MPa; Tensile stress at yield 70-75 MPa; Elongation at break 55%; Flexural modulus 2700-2720 MPa; Flexural strength 97 MPa; Charpy notched impact strength 15 kJ/m²; Izod notched impact strength 130 J/m; Heat deflection temperature 163-172°C at 0.45 MPa, 100-130°C at 1.8 MPa; Coefficient of linear thermal expansion 1.0E-4 cm/cm/°C; Specific heat 1470 J/kg/°C; Thermal conductivity 0.23 W/m/K; Surface resistivity 1E16-1E17 ohms; Volume resistivity 1E15-1E16 ohm·cm; Dielectric strength 18 kV/mm; Dielectric constant 3.80 (1 MHz); Dissipation factor 7.0E-3 (1 MHz); Arc resistance 250 s; UL flammability rating HB.
Uses:Mainly used to manufacture gears, conveyor machine parts, engineering parts and fasteners, as well as housings, bearings and other components in automotive applications.
Technical Specifications:
Density: 1.42 g/cm³ (ASTM D792/ISO 1183)
Melt flow rate: 1.7 g/10min (190°C/2.16kg, ISO 1133)
Tensile strength (yield): 70.0 MPa (ISO 527-2)
Heat deflection temperature: 130°C at 1.8 MPa (ASTM D648)
Flammability rating: HB (UL 94, 0.8mm/1.5mm)
共 1 家生产厂家、批发商，
1 条供应报价
供应报价
常见问题
- POM 2010的 CAS 号是多少？
- POM 2010的 CAS 号是 None。
- POM 2010的分子式和分子量是什么？
- POM 2010的分子式为 (CH2O)n。
- POM 2010的英文名称是什么？
- POM 2010的英文名称为 Polyoxymethylene (POM) 2010。
- POM 2010还有哪些别名？
- POM 2010又称 聚甲醛树脂、聚缩醛树脂、POM。
- POM 2010有哪些供应商和生产厂家？
- 掌上化工当前收录 1 条POM 2010供应报价，来自 1 家供应商，可按地区、纯度、级别筛选对比。
- POM 2010的供应商主要分布在哪些地区？
- POM 2010的供应商主要分布在 上海市（1 条） 等地。
- POM 2010有哪些级别可选？
- 平台上POM 2010的供应级别包括 工业级。
- POM 2010的报价单位是什么？
- POM 2010的报价单位主要有 千克。
- 哪里可以查到POM 2010的价格？
- 掌上化工POM 2010产品页汇总了各供应商的最新报价与规格，地址：/chemicals/pom-2010/。部分供应商价格为电议，可通过页面上的询价功能直接获取。
以上信息由平台根据收录的产品数据自动生成，数据更新时间 。 价格与库存由供应商自行发布，实际交易请以询价结果为准。
没找到合适的供应商？
发布采购需求，让供应商主动联系你。我们会在 1 个工作日内跟进。
发布POM 2010采购需求