EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型 (CAS No.None)
- 中文别名
- 热熔级EVA；增韧级EVA；薄膜级EVA；结构发泡EVA
- 英文名称
- EVA 210W (Ethylene-Vinyl Acetate Copolymer)
- 分子式
- (C2H4)x(C4H6O2)y
- 所属类别
- 塑料橡胶
- 物化性质
- 白色半透明颗粒，醋酸乙烯含量28wt%，密度0.951g/cm³，熔融峰值温度约60°C，维卡软化温度约39°C，熔体流动速率（190°C/2.16kg）400g/10min，加工温度低于230°C，不溶于水，具有良好的韧性和热熔粘接性。
- 密度
- 0.951g/cm³（ASTM D792, ISO 1183）
English description（英文原文，共 1173 字符）
Product Name:EVA 210W (Ethylene-Vinyl Acetate Copolymer)
English Name:EVA 210W (Ethylene-Vinyl Acetate Copolymer)
CAS No.:24937-78-8
Aliases:Hot-melt grade EVA, Toughened grade EVA, Film grade EVA, Structural foam EVA
Molecular Formula:(C2H4)x(C4H6O2)y
Physical Properties:White translucent pellets, vinyl acetate content 28wt%, density 0.951 g/cm³, melting peak temperature about 60°C, Vicat softening temperature about 39°C, melt flow rate 400 g/10min (190°C/2.16kg), processing temperature below 230°C, insoluble in water, with good toughness and hot-melt adhesion.
Uses:Used in wire jacketing, compounding industry, mixed sealants and adhesives. Suitable for processes such as blow molding, compound extrusion, structural foam molding, sheet extrusion, compression molding and injection molding. Widely applied in hot-melt adhesives, films and toughening modification materials.
Technical Specifications:
Vinyl acetate content: 28.0wt%
Density: 0.951 g/cm³ (ASTM D792, ISO 1183)
Melt flow rate: 400 g/10min (190°C/2.16kg, ASTM D1238, ISO 1133)
Vicat softening temperature: 39.0°C (ASTM D1525, ISO 306)
Melting peak temperature: 60.0°C (ASTM D3418, ISO 3146)
English Name:EVA 210W (Ethylene-Vinyl Acetate Copolymer)
CAS No.:24937-78-8
Aliases:Hot-melt grade EVA, Toughened grade EVA, Film grade EVA, Structural foam EVA
Molecular Formula:(C2H4)x(C4H6O2)y
Physical Properties:White translucent pellets, vinyl acetate content 28wt%, density 0.951 g/cm³, melting peak temperature about 60°C, Vicat softening temperature about 39°C, melt flow rate 400 g/10min (190°C/2.16kg), processing temperature below 230°C, insoluble in water, with good toughness and hot-melt adhesion.
Uses:Used in wire jacketing, compounding industry, mixed sealants and adhesives. Suitable for processes such as blow molding, compound extrusion, structural foam molding, sheet extrusion, compression molding and injection molding. Widely applied in hot-melt adhesives, films and toughening modification materials.
Technical Specifications:
Vinyl acetate content: 28.0wt%
Density: 0.951 g/cm³ (ASTM D792, ISO 1183)
Melt flow rate: 400 g/10min (190°C/2.16kg, ASTM D1238, ISO 1133)
Vicat softening temperature: 39.0°C (ASTM D1525, ISO 306)
Melting peak temperature: 60.0°C (ASTM D3418, ISO 3146)
共 1 家生产厂家、批发商，
1 条供应报价
供应报价
常见问题
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的 CAS 号是多少？
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的 CAS 号是 None。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的分子式和分子量是什么？
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的分子式为 (C2H4)x(C4H6O2)y。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的英文名称是什么？
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的英文名称为 EVA 210W (Ethylene-Vinyl Acetate Copolymer)。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型还有哪些别名？
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型又称 热熔级EVA、增韧级EVA、薄膜级EVA、结构发泡EVA。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型有哪些供应商和生产厂家？
- 掌上化工当前收录 1 条EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型供应报价，来自 1 家供应商，可按地区、纯度、级别筛选对比。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的供应商主要分布在哪些地区？
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的供应商主要分布在 上海市（1 条） 等地。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型有哪些级别可选？
- 平台上EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的供应级别包括 工业级。
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的报价单位是什么？
- EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的报价单位主要有 千克。
- 哪里可以查到EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型的价格？
- 掌上化工EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型产品页汇总了各供应商的最新报价与规格，地址：/chemicals/eva-210w-re-rong-ji-zeng-ren-ji-bao-mo-ji-jie-gou-fa-pao-cheng-xing/。部分供应商价格为电议，可通过页面上的询价功能直接获取。
以上信息由平台根据收录的产品数据自动生成，数据更新时间 。 价格与库存由供应商自行发布，实际交易请以询价结果为准。
没找到合适的供应商？
发布采购需求，让供应商主动联系你。我们会在 1 个工作日内跟进。
发布EVA 210W 热熔级 增韧级 薄膜级 结构发泡成型采购需求